Optical and spectral properties | |
---|---|
Transmission range in µm (minimum 10%) | 0,12‐11,8 |
Transmission range in µm (minimum 50%) | 0,13‐10,5 |
Refractive index @633nm | 1,432888 (1,39908 @5µm) |
Reflection losses in % at 1 surface | 2,89 @4µm
|
Reflection losses, % for two surfaces | 5,4 @5µm
|
dN/dT in 1/K | -10,6 · 10-6
|
Physical properties | |
---|---|
Density in g/cm3 | 3,18
|
Melting point in °C | 1418 |
Specific heat capacity in J/(kg · K) | 854 |
Thermal conductivity in W/(m · K) | 9,71
|
Thermal expansion in 1/K | 18,9 · 10-6
|
Dielectric constant | 6,76
|
Solubility in water in g/100g | 0,16 · 10-4 @25°C |
Mohs hardness | 4
|
Knoop hardness in kg/mm² | 163
|
Material type | single crystalline, synthetic
|
Crystal type | cubic, face-centered |
Crystal structure | cF12
|
Lattice constant in Å | a = 5,46
|
Elastic coefficient in GPa | C11 = 165 C12 = 47 C44 = 33,9 |
Young's Modulus (E) in Gpa | 75,8 |
Shear Modulus (G) in GPa | 33,7 |
Bulk Modulus (K) in GPa | 82,71 |
Rupture Modulus in MPa | 40
|
Apparent elastic limit in MPa | 36,5
|
Poisson's ratio | 0,29 |
Spectral properties |
---|
sample thickness: 2 mm |
Optical and spectral properties | |
---|---|
Transmission range @10% min. | 0,12 - 11,8 |
Transmission range @50% min. | 0,13 - 10,5 |
Brechungsindex @ 633nm | 1,432888 (1,39908 @5µm) |
Reflection losses in % at 1 surface | 2,89 @ 4µm |
Reflection losses, % for two surfaces | 5,4 @ 5µm |
dn/dT in 1/K | -10,6 · 10-6 |
Physical properties | |
---|---|
Density in g/cm³ | 3,18 |
Melting point in °C | 1418 |
Specific heat capacity in J/(kg · K) | 854 |
Thermal conductivity in W/(m · K) | 9,71 |
Thermal expansion in 1/K | 18,9 · 10-6 |
Dielectric constant | 6,76 |
Solubility in water in g/100g | 0,16 · 10-4 @ 25°C |
Mohs hardness | 4 |
Knoop hardness in kg/mm² | 163 |
Material type | single crystalline, synthetic |
Crystal type | kubisch flächenzentriert |
Crystal structure | cF12 |
Lattice constant in Å | a = 5,46 |
Elastic coefficient in GPa | C11 = 165 C12 = 47 C44 = 33,9 |
Young's Modulus (E) in Gpa | 75,8 |
Shear Modulus (G) in GPa | 33,7 |
Bulk Modulus (K) in GPa | 82,71 |
Rupture Modulus in MPa | 40 |
Apparent elastic limit in MPa | 36,5 |
Poisson's ratio | 0,29 |
Spectral properties | |
---|---|