Optical and spectral properties | |
---|---|
Transmission range in µm (minimum 10%) | 0,18‐6,4
|
Transmission range in µm (minimum 50%) | 0,2‐6,2 |
Refractive index @633nm | 1,829
|
Reflection losses in % at 1 surface @3µm | 7,9
|
dN/dT in 1/K | 5 · 10-6
|
Physical properties | |
---|---|
Density in g/cm3 | 4,56
|
Melting point in °C | 1950
|
Specific heat capacity in J/(kg · K) | 628
|
Thermal conductivity in W/(m · K) | 13,1
|
Thermal expansion in 1/K | 7,8 · 10-6 (111) 7,9 · 10-6 (110) 8,2 · 10-6(100) |
Dielectric constant | 7,75
|
Solubility in water in g/100g | insoluble |
Mohs hardness | 8‐8,5 |
Knoop hardness in kg/mm² | 1350 <100> |
Material type | single crystalline, synthetic
|
Crystal type | cubic |
Crystal structure | m3m
|
Lattice constant in Å | a = 10
|
Elastic coefficient in GPa | C11 = 333 C12 = 111 C44 = 114 |
Young's Modulus (E) in Gpa | 280
|
Shear Modulus (G) in GPa | 113 |
Bulk Modulus (K) in GPa | 180 |
Rupture Modulus in MPa | 150
|
Elastizitätsgrenze in MPa | 280
|
Poisson's ratio | 0,17 |
Spectral properties | |
---|---|
sample thickness: 1 mm |